Quick Details

  • Place of Origin: Guangdong, China (Mainland)
  • Brand Name: Hong Ye Silicone Rubber
  • Model Number: HY-6 series silicone rubber, molding silicone rubber
  • HARDNESS: 25-40 shore A
  • color: white
  • Mixing Ratio: 3%-5%
  • Appearance: Fluid silicone rubber
  • EINECS No: 39100000
  • Purity: 100%
  • Curing agent: 4% for free
  • Sample: 1kg free of charge
  • modes of transport: by sea or by air

Packaging & Delivery

Packaging Details: 25kg/drum,200kg/drum
Delivery Detail: Shipped in 4 days after payment

                          Good fluidity rtv2 silicone rubber for GRC molds

 

 Appilication of   Good fluidity rtv2 silicone rubber for GRC molds

 

Tin cure silicone rubber for making gypsum mold  is widely used for PU foaming, PU molding, resin handicraft decoration and the copy of archaize furniture, ceramics, craft candles, artificial statue, art reproduction, artificial imitated natural stone, shoes mold, lighting art, PU foaming resin and low melting point alloy materials moulds and etc.

 

Description of  Good fluidity rtv2 silicone rubber for GRC molds

 

Tin cure silicone rubber for making gypsum molds  is white or red flowing liquid with general hardness of 25-40A°after curing. Hongye mold making liquid silicon rubber is a kind elastic silicon rubber mold which features with resistance to deformation, high-temperature, acid-alkali and expansion as well as high reproduction times, good tensile strength, tear strength and elongation.

 

Features of  Good fluidity rtv2 silicone rubber for GRC molds

 

Good fluidity and good operability

Excellent mechanical properties, in particular tear strength and tensile strength.
Excellent flexibility

High temperature resistance, high duplication times and repeated use.

 

Instruction of Good fluidity rtv2 silicone rubber for GRC molds:

Add curing agent of 2%-3% at the room temperature, the silicone rubber is still operational within 30 minutes, and in 2-3 hours.

1. Adding curing agent 1%, the silicone rubber can still be operated within 2.5 hours and can be Demoulded after 6-8 hours.

2. Adding curing agent 2%, the silicone rubber can still be operated within 50 minutes to 1 hour and can Be demoulded after 2-3 hours.

3. Adding curing agent 3%, the silicone rubber can still be operated within 28 - 30 minutes and can bedemoulded after 1.5-2 hours.

4. Adding curing agent 4%, the silicone rubber can still be operated within 10 - 15 minutes and can be demoulded after 1 -1.5 hours. 

 

Datasheet for  Good fluidity rtv2 silicone rubber for GRC molds         

HY-6 series n of Condensation type silicone rubber

 

Frequently asked questions of   Good fluidity rtv2 silicone rubber for GRC molds

 Why does the liquid silicone rubber for gpusm products’mold making mold get burnt out?
The unsaturated resin produces great heat when added the curing agent. So you must demould the product within 3 minutes to avoid this problem.

 

 

 

Transaction History of the Supplier

Below is the information about the supplier's transactions conducted via Alibaba.com. If you require further details regarding the transaction data, please contact the supplier directly.

Transaction Overview

Transactions

Transaction Details

This supplier has completedtransactions with buyers from .

Shipping Destination
Transaction Value
Transaction Date
Email to this supplier
The supplier supports Trade Assurance – A free service that protects your orders from payment to delivery.
Supplier's Trade Assurance Limit: US $
Learn More